Shenzhen Feiyang Protech Corp., Ltd.
Shenzhen Feiyang Protech Corp., Ltd. Polyaspartic Polyurea Materials Researcher and Manufacturer
Add to Cart
F220 Polyaspartic Ester Resin
1)Description:
This is a new type of resin formulation that allows you to have your floor cleaned, prepared and painted within a single day. Uniquely developed, this technology is a revolution in floor coatings that has only been made possible by recent developments in polyaspartic resin technology. Our unique formulation uses this incredibly versatile resin to produce a high grade, high performance paint for heavily used areas both inside and outside. It’s also available in an anti slip finish. The anti slip particles are pre-blended (in the resin) which makes it easier to clean and to achieve a uniform finish.
Ⅰ Chemical formula and molecular weight
● Chemical Name: Aspartic Acid, Polyaspartic Polyurea Resin, N,N'-[2-methy-1,5-pentanediyl)]bis-, 1,1',4,4'-tetraethyl Ester
● ELINCS No.: 433-260-2
● CAS No.: 168253-59-6
Ⅱ Properties and application
● FEISPARTIC F220 is reactive partner for polyisocyanates, is a solvent free amine-functional resin. FEISPARTIC F220 is the same model as NH1220,could be used for the formulation of tough but flexible, lightfast and highly reactive two-component polyurethane spray coatings.
●FEISPARTIC F220 can be applied in SPUA (spraying elastomeric polyurea) R component as chain extender and main resin,FEISPARTIC F220 can be used to formulate anti-corrosion coatings for the protection of steel structures, oil pipelines, bubble landscape, concrete waterproofing materials.
● Main Feature
1. 100% high solid resin,
2. Faster drying time , Touch dry time with HDI is 5min,
3. Excellent flexibility, Good leveling properties,
4. Great weather, water and chemical resistance,
5. Excellent wearing resistance (abrasion loss ≤ 20 mg (500r/750g)),
6. Good adhesion on plastics e.g, ABS, PC, PVC, and various metals.
Ⅲ Quality standard
| INDEX | VALUE |
| Appearance | Colorless to light yellow green transparent liquid |
| Hazen | ≤250 |
| Solid Content /％ | 97±2 |
| Amine value(mg KOH/g) | 230-250 |
| Amine Equivalent(g/mol) | 230 |
| Hydroxyl value Equivalent(%) | 7.4 |
| Viscosity(mpa.s/25℃) | 60-100 |
| Relative density (25℃) | 1.05±0.02 |
Polyaspartic Property Advantage
| Property | Polyaspartic polyurea | Conventional polyurethane | Spray polyurea |
| Environmental property | Environmental friendly, construction solid content 70%-100% | Poor environmental protection, construction solid content 30%-40% | Good environmental protection, construction content 100% |
| Reaction speed | Curing time adjustive,20min-4h, normally cure in 15-℃ | Low reaction speed, request curing temperature above 5-℃, curing time more than 24h in normal temperature | Rapid curing speed, from seconds to tens of seconds |
| Adhesion with substrate | Don’t need primer, the adhesion with carbon steel substrate is beyond 14Mpa, the adhesion with concrete reach 4.5Mpa. | Need primer, adhesion with carbon steel substrate less than 8MPa, adhesion with concrete is 2.5 Mpa | Need primer, low adhesion |
| Weather resistance | QUVA test reach 4000h | QUVA test is 1000h at most | Poor weather resistance,QUVA ＜200h |
| Film thickness | One time construction film 50μm&sh;1mm | One time construction film 50μm&sh;&sh;100μm | One time construction film 0.6mm-2mm |
| Mechanical properties | Rigidity hardness 2H,elongation 400%, tensile strength 25MP | Rigidity hardness 2H,elongation 400%, tensile strenght 3MPa | Same as aspartic polyurea |
| Construction | Multiple construction method, get rid of the restriction of specified equipment | Same as aspartic polyurea | Relying on large special equipment |
Feiyang Feispartic Resin in Various Applications
| Application | F420 | F520 | F524 | F220 | F221 | F321 | F525 | F421 | F330 | F2850 | F2872 | D2905 | D2903 |
| Anti-corrosion Coating | √ | √ | √ | √ | √ | √ | √ | √ | |||||
| Waterproof Coating | √ | √ | √ | √ | √ | √ | √ | ||||||
| Flooring Coating | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | ||
| Wood Coating | √ | √ | √ | √ | √ | ||||||||
| Adhesive&Other | √ | √ | √ | √ | √ | √ | √ | √ |