Rigid Self-leveling Polyaspartic Flooring Coating Feature & Guide Formulation
Part I
* Technical Data
| No. | Item | Result | |
| 1 | Solid content % | 97 | |
| 2 | Fineness,um | 30 | |
| 3 | Pot life,min | 35 | |
| 4 | Dry time/h | Touch dry | 42min |
| Hard dry | 24h | ||
| 6 | Tensile strength,MPa | 40 | |
| 7 | Elongation at break,% | 9% | |
|
| Hardness(Shore D) | 75 | |
| 8 | Flexibility at low temp(-20℃),mm | 6cm | |
|
| Abrasion Resistance (1KG/1000,mg) | 21mg | |
* Gloss Stablility Testing
| After Mix | 0 min | 5 min | 10min | 15min | 20min | 25min | 30min |
| Final gloss | 92 | 92 | 91.5 | 92 | 91.5 | 91.5 | 91.5 |
Part II
* Component A (Paint)
| Material Name | Content (%) |
| F420 Polyaspatic Resin | 25 |
| F520 Polyaspartic White plasm | 26 |
| F520 Polyaspartic Resin | 18 |
| F524 A3 Polyaspartic A3 plasm | 12 |
| F524 Polyaspartic Resin | 15 |
| H15 Dustproof Agent | 0.3 |
| BD8330 Dispersant | 0.2 |
| 2722 Anti-foam Agemt | 0.8 |
| 3600 Leveling Agent | 0.2 |
| KH560 Coupling Agent | 2.5 |
* Component B (Hardener)
| Material Name | Content (%) |
| N3390 | 70 |
| HMDI | 20 |
| GB905-85 | 10 |
* Ratio A:B=1:0.5